What are the mechanical properties of 20MnB5 notch-toughness test

What are the mechanical properties of 20MnB5 notch-toughness test

What are the mechanical properties of 20MnB5 notch-toughness test

Our company is a large 20MnB5 notch-toughness test steel enterprise integrating steel plate production, sales and processing. It is a first-class agent of Shanxi Taigang, Shanghai Baosteel, Jiugang, Xi'an Huaxin, Taishan steel, Dongfang special 20MnB5 notch-toughness test steel and southwest special steel. It is a special dealer of famous steel plants in China, such as Columbus, NAS, acerinox, Outokumpu, Arcelor, nipponmetalindustry, nipponyakinkogyo, NSC, etc.

S45C steel plate chemical composition: C 0.42~0.48, Si 0.15~0.35, Mn 0.60~0.90, P≤0.030, S≤0.035, Cu≤0.30, Ni≤0.20, Cr≤0.20
Mechanical properties of 20MnB5 notch-toughness test product
Tensile strength>686MPa
Yield strength>490MPa
Elongation δ5>17%
Shrinkage ψ>45%
Impact toughness value>78J/cm2
The hardness is 201~269HB.

Different form 20MnB5 notch-toughness test, room temperature and medium temperature boiler steel shall have those advantages:Higher room temperature strength;Good impact toughness and low notch sensitivity;As the drum and other parts require a lot of cold deformation during processing, room temperature and medium temperature boiler steel must have good aging toughness;Good processing technology and welding performance;Good macrostructure, etc.

After adding trace elements such as phosphorus, copper, chromium, and nickel to Q355NH steel, a dense and highly adherent protective film is formed on the surface of the weathering steel, which prevents rust from spreading and developing, and protects the substrate under the rust layer to slow its corrosion . An amorphous spinel oxide layer of about 50 μm to 100 μm thick formed between the rust layer and the substrate is dense and has good adhesion to the base metal, which greatly improves the atmospheric corrosion resistance of the steel material, 20MnB5 notch-toughness test.

20MnB5 notch-toughness test, P355GH plate mechanical properties: P355GH steel plate thickness/mm:> 60-100: tensile strength σb / MPa: 490-630; yield strength σx / MPa:> = 315 Impact absorption energy AKv / J:> = 34. Steel plate thickness / mm:> 100-150: tensile strength σb / MPa: 480-630,y ield strength σx / MPa:> = 295 Impact absorption energy AKv / J:> = 34. Chemical composition % (C:0.10-0.22, Si:<=03.60, Mn:1.00-1.70, Nb:<=0.010, Ti:<=0.03 S:<=0.030, P:<=0.025, Cr:<=0.30, Ni:<=0.30, Cu:<=0.30, Mo:<=0.10, V <=0.02)

If you want to find wear resistant steel plates or abrasion resistant steel supplier and exporter in China, please visit us. We are one of the leading 20MnB5 notch-toughness test wear resistant steel plates manufactures and stock keepers. We have large stocks for wear resistant steel plates of various grades and dimension. We can not only send offer at the first time, but can also provide technical support and give you professional suggestions and answers about NM400 20MnB5 notch-toughness test steel specifications, difference between hardox 400 and AR400 and so on question about wear resistant steel plates. Come on! Just call us or send email.

The company formulates clear service process and service standard. To do a good job in after-sales service, first of all, clear service process and service standards should be formulated to let employees know which procedures to perform and which service standards to abide by.